核电是现在以及未来稳定可靠的清洁能源,是节能减排的重要力量，只有将核电站保温设计更合理，采用导热系数更低、稳定性更好的保温材料，减少热量损失，才能为国家节能减排起到积极带动作用。核级涂料是用于存在核辐射的场所和结构的防护涂料，ASTM E1530涂料导热系数测试标准/导热系数测试标准涂料的保温隔热性能一个非常重要的参考指标就是涂料导热系数测试结果，目前涂料导热系数测试标准主要为ASTM E1530标准，ASTM E1530-19为最新版本标准，已取代ASTM E 1530-11(2016)，南京睿督与美国权威实验室提供涂料ASTM E1530最新版本测试报告，咨询电话：025-8658 3475。
ASTM E1530导热系数-测试方法
This test method covers a steady-state technique for the determination of the resistance to thermal transmission (thermal resistance) of materials in thickness of less than 25mm. This test method is useful for materials having a thermal resistance in the range from 10 to 400 ×10-4 m2 k/w thermal conductivity in the approximate range, temperature range from 150 to 400K. It can be used outside these ranges with reduced accuracy for thicker specimens and for thermal conductivity values up to 60W/(M.K)
ASTM E 1530标准与ASTM C 518测试方法及概念类似。
ASTM E1530导热系数-样品要求
ASTM E1530样品要求：The recommended specimen configuration is a 50.8±0.25mm diameter disk, having smooth flat and parallel faces. The thickness less than 25mm.
导热系数（thermal conductivity）:热流密度与温度梯度之比。即在单位温度梯度作用下物体内所产生的热流密度，单位为W/(m (℃)。导热系数是指在稳定传热条件下，1m厚的材料，两侧表面的温差为1度（K,°C）,在1秒内，通过1平方米面积传递的热量，用λ表示，单位为瓦/米度（W/mK,此处的K可用℃代替）。
导热系数与材料的组成结构、密度、含水率、温度等因素有关。非晶体结构、密度较低的材料，导热系数较小。材料的含水率、温度较低时，导热系数较小。
通常把导热系数较低的材料称为保温材料(我国国家标准规定，凡是平均温度不高于350℃时导热系数不大于0.12W/(m/K)的材料称为保温材料），而把导热系数在0.05瓦/米摄氏度以下的材料称为高效保温材料。
核级涂料是用于存在核辐射的场所和结构的防护涂料，涉及辐射的厂房、设备和其它结构表面。安全壳是核电站的中心部位，应用涂料使用环境中存在大量的放射性物质、高辐射物、高放射性裂变产物的沾污;经常处在高温高湿条件下，暴露于去除放射性污染的试剂中，特别是在失水情况下，瞬间产生的高温高压伴随着大量的放射性物质形成的强辐射，同时喷淋高浓度硼酸水。因此，应用于核岛安全壳内的防护涂层不可以有严重的剥落、起壳、粉化。否则，大量的残余物进入堆内总应急冷却液中，导致管线、泵、喷嘴及堆总冷却管道堵塞，降低影响安全系统的功能，会带来严重的安全事故。因此，安全壳内钢结构用涂料必须经受耐辐照试验、去污试验和DBA试验的考核。
核电站所有的防护涂层，并不单单是为了防腐目的，更多的是为了核电站的安全运行。在防护涂层应用方面，不仅仅是通过LOCA试验、耐辐射和去污性能试验后就可以放心选用的，而且要有良好的核电站运行记录。